Effects of compacting activated carbons on their volumetric CO2 adsorption performance，
作者：Dawei Li*，Yu Wang，Xiaoxiao Zhang，Jiaojiao Zhou，Yonghong Yang，Zongbo Zhang，Yuanyu Tian*，Xuebo Zhao
關(guān)鍵字：CO2 capture；Activated carbon；Biomass；Volumetric performance；Density
論文來源：期刊
具體來源：Fuel，2020，262, 116540
發(fā)表時間：2020年
The practical application of activated carbons (ACs) in CO2 capture requires the materials to possess all-round high volumetric CO2 adsorption performance, but influences of compaction of ACs on the all-round volumetric adsorption performance are unclear. In this research, coconut shell-based and rice husk-based ACs were compacted to study the effects of compaction on ACs'' volumetric CO2 uptake, adsorption rate, and CO2/N-2 selectivity. The compaction increased ACs'' volume-based low-pressure CO2 uptake (by up to 53.8 wt%), atmospheric-pressure uptake (by up to 43.2%), CO2 adsorption rate, and CO2/N-2 selectivity, simultaneously. The main reason was that compaction changed the volumetric volume of micropores in various ranges (< 0.7 nm,< 1 nm, and < 2 nm). This change was because compaction increased tap density of ACs via reducing macropores in the range of 2 to 10 mu m and increasing carbon skeletal density. Compaction slightly affected ACs'' surface functional groups, gravimetric nanopore parameters, and gravimetric CO2 uptake. The research showed that compaction enhanced ACs'' all-round volumetric CO2 adsorption performance; this result was highly appealing for ACs'' practical application, but was not found in previous research.